Coefficient d'Expansion Thermique du Custer Spar avec ajouts de frittes Ferro 3110 et 3134

Some translations :
Coefficient d’Expansion Thermique du Custer
Spar avec ajouts de frittes Ferro 3110 et 3134.=
Thermal Expansion Coefficient of melted mixtures
(as fritted materials) based on Custer Spar
enriched by additions of Ferro frits 3110 and 3134.

T.E.C. en 10-7 °C. =
T.E.C in 10-7 °C.

Quantité de fritte ajoutée à 100 parties de Custer.=
Amount of frits added to 100 parts ofCuster Spar.

-----------------------------------------------------------------

Since the formulas of feldspars and feldspar-like
materials are somewhat similar to those of high
temperature glazes, we used this last principle as
a starting point to make a comparative study of
two frits on the Thermal Expansion Coefficient
(T.E.C.) of the potassium feldspar Custer.

It should be remembered that these expansions
(dilatations) are valid only if the « Custer +added
material» mixture is completely melted
(or transformed into a frit).
This is not valid for a paste (clay) where there would
remain non-molten crystalline materials and badly
amalgamated in the vitreous phase.

------------------------------------------------------------

Comme les formules des feldspaths et feldspathoïdes
sont quelque peu similaires à celles de glaçures de
haute température, nous avons utilisé ce dernier
principe comme point de départ pour faire une
étude comparative de l’influence de deux frittes
sur le Coefficient Thermique d’Expansion (T.E.C.)
du feldspath potassique Custer (USA).

Il faut retenir que ces dilatations ne sont valables
que si le mélange « Custer+matière ajoutée»
est fusionné complètement (ou transformé en fritte).
Cela n'est pas valable pour une pâte (argile) où il
resterait de la matière cristalline non fondue et
mal amalgamée dans le flux vitreux.

Smart.Conseil
http://perso.wanadoo.fr/smart2000/index.htm

Édouard Bastarache
http://www.flickr.com/photos/30058682@N00/