Viscosité théorique à l'Eutectique du Custer Spar avec ajouts de frittes Ferro 3110 et 3134

Some translations :
Viscosité théorique à l’Eutectique du Custer Spar
avec ajouts de frittes Ferro 3110 et 3134.=
Theoritical viscosity at the Eutectic of melted
mixtures (as fritted materials) based on Custer
Spar enriched by additions of Ferro frits 3110 and
3134.

Viscosité en Poises à l’Eutectique.=
Viscosity in Poises at the Eutectic.

Quantité de fritte ajoutée à 100 parties de Custer. =
Amount of frit added to 100 parts of Custer Spar.

--------------------------------------------------------------

Since the formulas of feldspars and feldspar-like
materials are somewhat similar to those of high
temperature glazes, we used this last principle as
a starting point to make a comparative study of
the effects of increasing amounts of Ferro frits
3110 1nd 3134 on the theoritical viscosity at the
eutectic of Custer feldspar.

It should be remembered that these data are valid
only if the « Custer+added material » mixture
is completely melted (or transformed into a frit).

------------------------------------------------------------------

Comme les formules des feldspaths et feldspathoïdes
sont quelque peu similaires à celles de glaçures de
haute température, nous avons utilisé ce dernier
principe comme point de départ pour faire une
étude comparative de l’influence de quantités
croissantes de deux frittes sur la viscosité théorique
à l'eutectique du feldpath potassique Custer (USA).

Il faut retenir que ces mesures ne sont valables
que si le mélange « Custer+matière ajoutée »
est fusionné complètement (ou transformé en
fritte).

Smart.Conseil
http://perso.wanadoo.fr/smart2000/index.htm

Édouard Bastarache
http://www.flickr.com/photos/30058682@N00/